SK Functional Polymer introduces its new Lotryl®17BA07T an Ethylene – Butyl Acrylate 17% copolymer with MFI 7g/10min (190°C,2.6kg) designed for Semi conductive and Insulation layer of Medium and High Voltage Cable.
Lotryl® eases the processability of cable compound and brings high toughness. These features will decrease the risk of electrical breakdown thanks to the reduction of protrusion during extrusion. Lotryl® polarity will also play a significant role in the slow down of water tree propagation along the insulation layer.
Lotryl® 17BA07T Typical Properties
Test MethodUnitTypical ValueButyl Acrylate ContentFTIR (internal method)%.-wt.17Melt index (190°C/2.16kg)ISO 1133 / ASTM D1238g/10min.7Melting PointISO 11357-3°C107DensityISO 1193 / ASTM D150g/cm30.94Vicat Softening Temperature (10N)1ISO 306 / ASTM D1525°C65Flexural Modulus1ISO 178 / ASTM D790MPa74Elongation at Break1ISO 527-2 / ASTM D638%800Tensile Strength at break1ISO 527-2 / ASTM D638MPa11Hardness Shore A/D1ISO 868 / ASTM D2240 93/331: On compression molded samples.